Electrostatic chuck having bonded structure and method of manufacturing the same

ABSTRACT

An electrostatic chuck having a bonded structure comprising a ceramic electrostatic chuck member, a metal member and a bonding layer; the bonding layer having at least a first most outer bonding layer being joined to the ceramic electrostatic chuck member, a second most outer bonding layer being joined to the metal member, and a polyimide layer as an intermediate layer disposed between the first and second most outer bonding layers, and each of the most outer bonding layers being made of a silicone layer or an acrylic layer, and a method for manufacturing the same are provided: the bonding layer being excellent in airtightness, bonding strength, and corrosion resistance, free from bleeding of a bonding material even under high pressures at time of joining, and the junction body being good in heat conductivity, and having a good flatness of its adsorption surface, with a small deformation due to temperature change.

BACKGROUND OF THE INVENTION AND RELATED ART STATEMENT

[0001] The present invention relates to an electrostatic chuck having a bonded structure formed by bonding a ceramic electrostatic chuck member and a metal member, and to a method of manufacturing thereof.

[0002] As shown in FIG. 2, an electrostatic chuck 25 having a bonded structure contains an electrostatic chuck member 10, a metal member 12 as a base material and a bonding layer 14. And, after a silicon wafer 16 is held (chucked) on the electrostatic chuck member 10 by electrostatic attraction, treatments such as CVD (chemical vapor deposition), sputtering, etching and the like are performed on a surface of the silicon wafer 16 within a system, for example, a CVD system, a sputtering system, an etcher and the like as it is. Further, an electrostatic chuck electrode 18 is embedded in the electrostatic chuck member 10 so that the electrostatic chuck member 10 is charged by applying a voltage from a terminal 20 thereto and the silicon wafer 16 is held with the chuck member by virtue of the resulting electrostatic attraction.

[0003] In the electrostatic chuck 25 having bonded structure comprising an electrostatic chuck member and a metal member as described above, when treatments such as CVD, sputtering, etching and the like are performed, which treatments use a plasma reaction, it becomes difficult to control film formation on the silicon wafer because temperature is increased in the silicon wafer due to heat input from the plasma. As a measure to solve the problem, there have been employed the mechanism for cooling the metal member 12, the method for cooling the electrostatic chuck member 10 and the metal member 12 by introducing Ar gas or N₂ gas 22 between the electrostatic chuck 10 and silicon wafer 16, or the like. In addition, when the treatments such as CVD, sputtering, etching and the like are performed, which treatments use a plasma reaction, the electrostatic chuck member 10, the metal member 12 and the bonding layer 14 are exposed to a chemically severe atmosphere.

[0004] In an electrostatic chuck, there have conventionally been known, as a method of fixing an electrostatic member to a metal member, a method of using a mechanical clamp structure with clamps and bolts, a method of using an organic adhesive or glass as a bonding layer, and the like. When a bonding layer is used, because the bonded structure for an electrostatic chuck is exposed to a chemically severe atmosphere as described above, the bonding layer is required to have good heat conductivity, airtightness, corrosion resistance, and further flatness of the electrostatic chuck member after being bonded, as well as high bonding strength.

[0005] In recent years, although ceramic electrostatic chuck members have been widely used, their low mechanical toughness makes it difficult to fix them by mechanical methods such as the use of the mechanical clamp structure and the like. In the case where a general organic adhesive was used, there was a problem that strain and cracks were caused in the surface of the ceramic electrostatic chuck member during use in a wide temperature range, and in the case where glass was used, there was a problem that deformation of a metal member was generated because a high temperature was required for bonding.

[0006] In order to solve these problems, JP-A-4-287344 has proposed a bonded structure using a silicone resin in a paste form as a bonding layer, and JP-A-3-3249 has proposed a bonded structure using indium as a bonding layer.

[0007] However, in the case where a ceramic electrostatic chuck member and a metal member are bonded using a silicone resin in a paste form or indium as a bonding layer, if bonding pressure is low, a defect will be caused in the bonding, resulting in some problems in reliability of bonding strength and airtightness. On the other hand, if bonding pressure is high, there was caused a problem of making the bonding material bleed out from the joint surface. Moreover, there was such a problem that the flatness of the electrostatic chuck member was deteriorated after bonding due to a difference in thermal expansion between the electrostatic chuck member and the metal member.

SUMMARY OF THE INVENTION

[0008] The present invention has been made to solve the above described problems and is aimed at providing an electrostatic chuck having a bonded structure, in which airtightness, bonding strength and corrosion resistance of a bonding layer are good, the problem of bleeding out the bonding material under high pressures at the time of bonding is solved, and further the electrostatic chuck having a bonded structure is good in heat conductivity, shows a small deformation due to temperature change, and is good in flatness of an adsorption surface, so that it can be used in applications where high precision and high reliability are required, and providing a method of manufacturing the same.

[0009] According to the present invention, there is provided a n electrostatic chuck having a bonded structure comprising a ceramic electrostatic chuck member, a metal member, and a bonding layer; said ceramic electrostatic chuck member and the metal member being bonded with said boding layer,

[0010] wherein said bonding layer has at least a first most outer bonding layer being bonded to said ceramic electrostatic chuck member, a second most outer bonding layer being bonded to said metal member, and a polyimide layer being disposed between said first and second most outer bonding layers, and each of first and second most outer bonding layers is made of either a silicone layer or an acrylic layer.

[0011] Further, according to the present invention, there is provided a method of manufacturing n electrostatic chuck having a bonded structure comprising a ceramic electrostatic chuck member, a metal member, and a bonding layer; said ceramic electrostatic chuck member and the metal member being bonded with said boding layer,

[0012] wherein said bonding layer has at least a first most outer bonding layer being bonded to said ceramic electrostatic chuck member, a second most outer bonding layer being bonded to said metal member, and a polyimide layer being disposed between said first and second most outer bonding layers, and each of most outer bonding layers is made of either a silicone layer or an acrylic layer;

[0013] wherein said method comprises the steps of:

[0014] preparing a sheet comprising at least a first most outer layer, second most outer layer made of either a silicone layer or an acrylic layer, and an intermediate layer being disposed between said first and second most outer layers and made of a polyimide layer,

[0015] vacuum-packing said electrostatic chuck member, said bonding layer, said metal layer and said sheet being sandwiched between said electrostatic chuck member and said metal member into a vacuum-packing bag; and

[0016] heating thus vacuum-packed electrostatic chuck member, bonding layer and metal layer under isotropic pressurization to bond them firmly.

BRIEF DESCRIPTION OF THE DRAWINGS

[0017]FIG. 1 is a sectional view showing one embodiment of a bonding layer to be used in the present invention.

[0018]FIG. 2 is a section explaining view showing the state in which a silicon wafer is held with a bonded structure for an electrostatic chuck according to the present invention.

[0019]FIG. 3 (a), FIG. 3 (b), and FIG. 3 (c) show illustratively the steps of a method of manufacturing an electrostatic chuck having a bonded structure according to the present invention, and FIG. 3 (a) shows a prebonding step, FIG. 3 (b) shows a vacuum packing step, and FIG. 3 (c) shows an isotropic pressurization step.

[0020]FIG. 4 is a graph showing the schedules of isotropic pressurization and heating.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENT

[0021] In the following, the present invention will be described based on the drawings according to the embodiments, but the present invention will not limited to these embodiments.

[0022]FIG. 1 shows an embodiment of a bonding layer that is a characteristic feature in an electrostatic chuck having a bonded structure according to the present invention. As shown in FIG. 1, a bonding layer 5 has at least a first most outer bonding layer 1 being joined to a ceramic electrostatic chuck member 10 (see FIG. 2), a second most outer bonding layer 2 being joined to a metal member 12 (see FIG. 2) and a polyimide layer 3 being disposed between the first and second most outer bonding layers 1 and 2, and each of first and second most outer bonding layers 1 and 2 is composed of a silicone layer or an acrylic layer.

[0023] In an electrostatic chuck having a bonded structure according to the present invention, because the bonding layer has a constitution as described above, the bonding layer shows good airtightness, good bonding strength and good corrosion resistance, and the bleeding out problem of the bonding material at the time of bonding can be practically eliminated. In addition, the bonded structure of the present electrostatic chuck is good in heat conductivity, and it shows a small deformation due to temperature change. Therefore, the present electrostatic chuck can show a good flatness of an adsorption surface. Accordingly, the present electrostatic chuck having a bonded structure can be used in applications where high precision and high reliability are required.

[0024] Each member composing a bonding layer used in the present invention will be described. The first and second most outer bonding layers 1 and 2 are comprised of a silicone layer or an acrylic layer. Both of the first and second most outer bonding layers 1 and 2 may be the same acrylic layer or silicone layer, and any one of them may be an acrylic layer and the other may be a silicone layer.

[0025] The polyimide layer 3 being disposed between the first and second most outer bonding layers 1 and 2 is mainly composed of a polyimide. A polyimide is a high molecular substance having an acid imide bond in the main chain and preferably has 50 mol % or more of a constitutional repeating unit expressed by formula (1) in the whole constitution of the polyimide.

[0026] [where, Ar1 contains at least one aromatic ring, and two carboxylic groups forming an imide ring are bonded to adjacent carbon atoms on the aromatic ring; Ar2 is an organic group and is preferable to contain an aromatic ring.]

[0027] More preferably, a polyimide has 50 mol % or more of a constitutional repeating unit expressed by formula (2) in the whole constitution of polyimide.

[0028] The acrylic layer is contained an acrylic resin as the main component. The acrylic resin is a general term for polymers obtained by polymerizing acrylic acid and its derivatives and includes polymers and copolymers of acrylic acid and its esters, acrylamide, acrylonitrile, methacrylic acid and its esters, and others, and which polymers and copolymers may be crosslinked or non-crosslinked. The silicone layer is contained a silicone resin as the main component. The silicone resin is a polymer of a silicide having a siloxane bond as the main skeletal structure. The silicone resin may be crosslinked or non-crosslinked, and has, for example, a constitutional repeating unit comprising of a component of formula (3) and/or formula (4) as the main component.

[0029] (where R is H, CH₃, C₂H₅, C₆H₅ and the like)

[0030] (where R is H, CH₃, C₂H₅, C₆H₅ and the like)

[0031] The thickness of the bonding layer 5 is preferable to be 0.05 to 0.5 mm. This is because the flatness in the adsorption surface of the electrostatic chuck member 10 after being jointed becomes worse if the thickness of the bonding layer 5 is thinner than 0.05 mm, and it becomes difficult to transfer smoothly the heat in the electrostatic chuck member 10 to the metal member 12 if the thickness is larger than 0.5 mm. The thickness of the bonding layer 5 is more preferable to be 0.08 to 3.0 mm and is the most preferable to be 1.0 to 2.5 mm. The flatness of the electrostatic chuck member 10 can be made to be within 30 μm by making the thickness of the bonding layer 5 be 0.05 to 0.5 mm. The present electrostatic chuck having a bonded structure mentioned above may be used in applications requiring high precision and high reliability by making the flatness of the electrostatic chuck be within 30 μm.

[0032] The method of measuring the flatness will be described in the following. An electrostatic chuck member was put upward on a surface plate and the height of the surface of the electrostatic chuck member was measured with a height gage. As the measured points, total 17 points including the starting point, that is, the center of the electrostatic chuck as the starting point and each 8 points in the direction X-to-Y were measured, and the difference between the maximum measured value and the minimum measured value was defined as the flatness.

[0033] Moreover, in the first and second most outer bonding layers 1 and 2, and in the polyimide layer 3, particulate or squamous fillers having good thermal conduction may be dispersed in order to improve their heat conduction. As materials of the fillers, ceramics like alumina, aluminum nitride and SiC, metals like Al are good, and their size is good to be 0.5 μm to 50 μm, and the content of the fillers is good to be 50 vol. % or less.

[0034] In the next place, other members composing the present electrostatic chuck having a bonded structure will be described.

[0035] The electrostatic chuck member 10 is comprised of a ceramic material, for example, aluminum nitride (AlN), alumina (Al₂O₃), calcium titanate (CaTiO₃), or barium titanate (BaTiO₃), and is preferably comprised of aluminum nitride (AlN).

[0036] An electrostatic chuck electrode 18 is embedded in the electrostatic chuck member 10. It is preferable to embed the electrode during sintering electrostatic chuck member to form the electrostatic chuck member with the electrostatic chuck electrode as an integrated body from the antiflaking point of view and the like during its applications. The surface of the electrostatic chuck member 10 is charged by applying a voltage to the electrostatic electrode 18 through the terminal 20, resulting in the generation of electrostatic attraction, with which attraction silicon wafer 16 can be adsorbed on the adsorption surface, the upper surface of the electrostatic chuck member 10.

[0037] The metal member 12 supporting the electrostatic chuck member 10 serves to remove the heat in the electrostatic chuck member 10 and is comprised of, for example, aluminum, brass and others. More, in the electrostatic chuck member 10 and metal member 12 of the electrostatic chuck having a bonded structure 25, one may make a hole for a cooling medium 24 to pass a cooling medium, for example, argon gas (Ar gas), nitrogen gas (N2 gas) and the like. Further, instead of this, or in addition to this, the metal member 12 may be provided with an other cooling mechanism, for example, a water cooling mechanism and the like.

[0038] Next, one example of the manufacturing method of an electrostatic chuck having a bonded structure according to the present invention will be described in accordance with FIG. 3 (a) to FIG. 3 (c).

[0039] First of all, using a sheet having at least three layers in which two most outer layer are comprised of a silicone layer or acrylic layer and a polyimide layer is disposed between them as a bonding layer, an electrostatic chuck member 32 and a metal member 34 are prebonded to prepare a prebonded body as shown in FIG. 3 (a). Then, as shown in FIG. 3 (b), this prebonded body is vacuum packed into a bag. Vacuum packing can be carried out with a commercially available vacuum packer. With a vacuum packer, the prebonded body is put into, for example, a heat-resistant tubular film 33 both ends of which are open, and one of the openings is blocked up and air is let out from the other opening, then the other opening is blocked to make a vacuum packing of the prebonded body in a sealed state with a bag made of the heat-resistant tubular film 33. Next, as shown in FIG. 3 (c), the vacuum packed prebonded body is heated and cooled under isotropic pressurization in an isotropic pressure device, including an autoclave, and the electrostatic chuck member 32 and the metal member 34 are bonded to manufacture an electrostatic chuck having a bonded structure according to the present invention.

[0040] An autoclave can be favorably used in the present invention because isotropic pressurization and heating can be performed at the same time. As conditions for isotropic pressurization and heating, for example, it is preferable to carry out the pressurization and heating in the schedules shown in FIG. 4. That is, it is preferable to maintain the autoclave at pressures of 5 to 20 atm and at temperatures of 100 to 150° C. for 1 to 5 hours.

EXAMPLE

[0041] In the following, the present invention will be described further in detail by examples, but the present invention should not be limited to these examples.

[0042] A sheet having at least three layers in which the two most outer layers were silicone layers and a polyimide layer was sandwiched between them was used as a bonding layer 30 in Example 1, and a sheet having at least three layers in which the two most outer layers were acrylic layers and a polyimide layer was sandwiched between them was used as a bonding layer 30 in Example 2. After each of the sheets was put between an electrostatic chuck member and a metal member and vacuum packed, the packed members were held in an autoclave at 120° C. under the pressure of 14 atm for 2 hours to be bonded.

[0043] On the other hand, using a silicone paste as an adhesive in Comparative example 1, after the paste had been applied to the surface of an electrostatic chuck member and the surface of a metal member in the thickness of 0.1 mm each through screen printing, the electrostatic member and the metal member were pasted together and held at 120° C. under atmospheric pressure for 2 hours to be bonded.

[0044] The flatness values of electrostatic members before and after bonding are shown in Table 1. All of the flatness values of electrostatic chuck members before bonding were 20 μm or less, but though the flatness values in Example 1 and Example 2 were hardly changed after bonding, the flatness value in Comparative Example 1 was increased to 100 μm or more. Further, the results of measuring the airtightness of the gas hole and bonded part using a He-leak detector showed good airtightness of 1E−9 Pa·m³/s or less in both Example 1 and Example 2. TABLE 1 Flatness of Flatness of Amount of electrostatic electrostatic leaked chuck members chuck members He Bonding (Before (After (After No. layer bonding) bonding) bonding) Example 1 Three layer 15.5 μm 14.3 μm 1.5E−10 sheet, Pa · m³/s silicone/ polyimide/ silicone Example 2 Three layer 18.3 μm 16.0 μm 1.7E−10 sheet, Pa · m³/s acrylic/ polyimide/ acrylic Comparative Silicone 17.5 μm 113 μm  Not Example 1 paste measured

[0045] As described above, if the bonded structure for the electrostatic chuck according to the present invention is employed, the boding layer shows a good airtightness, a good bonding strength and a good corrosion resistance. Furthermore, the bleeding out of a bonding material even under high pressures can be almost eliminated at the time of bonding them. In addition, the electrostatic chuck according to the present invention has a bonded structure being good in heat conductivity, and it shows only a small deformation, even temperature changes a great extent. Furthermore, the present electrostatic chuck is good in the flatness of its adsorption surface. Therefore, the present electrostatic chuck electrostatic chuck may be used in applications where high precision and high reliability are required. Moreover, when the present manufacturing method for an electrostatic chuck is used, it is possible to obtain a bonded structure practically free from the bleeding out problem of a bonding material under high pressures at the time of bonding the electrostatic chuck member and the metal member with the bonding layer. Accordingly, the bonding layer may provide a higher bonding strength and a good airtightness, with an excellent flatness of its electrostatic adsorption surface. 

What is claimed is:
 1. An electrostatic chuck having a bonded structure comprising a ceramic electrostatic chuck member, a metal member, and a bonding layer; said ceramic electrostatic chuck member and the metal member being bonded with said boding layer, wherein said bonding layer has at least a first most outer bonding layer being bonded to said ceramic electrostatic chuck member, a second most outer bonding layer being bonded to said metal member, and a polyimide layer being disposed between said first and second most outer bonding layers, and each of most outer bonding layers is made of either a silicone layer or an acrylic layer.
 2. The electrostatic chuck according to claim 1, wherein the thickness of the bonding layer is 0.05 to 0.5 mm.
 3. The electrostatic chuck according to claim 1, wherein the ceramic electrostatic chuck member has a base material made of aluminum nitride, and said base material is being formed as an integrated body by sintering it with an electrostatic chuck electrode being embedded thereinto.
 4. The electrostatic chuck according to claim 1, wherein flatness of an adsorption surface in the ceramic electrostatic chuck member is 30 μm or less.
 5. A method for manufacturing an electrostatic chuck having a bonded structure comprising a ceramic electrostatic chuck member, a metal member, and a bonding layer; said ceramic electrostatic chuck member and the metal member being bonded with said boding layer, wherein said bonding layer has at least a first most outer bonding layer being bonded to said ceramic electrostatic chuck member, a second most outer bonding layer being bonded to said metal member, and a polyimide layer being disposed between said first and second most outer bonding layers, and each of most outer bonding layers is made of either a silicone layer or an acrylic layer; wherein said method comprises the steps of: preparing a sheet comprising at least a first most outer layer, second most outer layer made of either a silicone layer or an acrylic layer, and an intermediate layer being disposed between said first and second most outer layers and made of a polyimide layer, vacuum-packing said electrostatic chuck member, said bonding layer, said metal layer and said sheet being sandwiched between said electrostatic chuck member and said metal member into a vacuum-packing bag; and heating thus vacuum-packed electrostatic chuck member, bonding layer and metal layer under isotropic pressurization to bond them firmly. 